Yglue™5401A/BDESCRIPTION: YGLUE™5404A/B is a special liquid resin system, which is used in electronic sealing. It is composed of electric filler, living diluents and super additives. Cured product has excellence gloss surface, similarity agate, its hardness, electric property , inflaming retarding are also very good.
RECOMMEND USAGE: YGLUE™5404A/B suit for the all need to sealing, encapsulation, insulating and damp-proof electrons or other kinds of products. Especially for the sealing of capacitance and transformer, or insulating of other electronics.
SURFACE PREPARATION: Ensure the surface preparations, and that the surface is clean and dry, free from dust, perfect degreasing. It is best that first chemical treatment, then coating, so can capture best adhesion.
APPEARANCE & CHARACTER:
YGLUE™5404A YGLUE™5404B
COLOR black liquid Brown liquid
VISCOSITY(25℃, cps) 1700-2000 30-100
SPECIFIC GRAVITY(25℃) 1.5-1.6 1.02
FLASH POINT(℃) 210 >240
MIX RATIO: YGLUE™5402A YGLUE™5402B
Weight ratio 4 1
POT LIFE: Pot life of mixing YGLUE™5404A and YGLUE™5404B , depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 30-40 minutes at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
25℃ 5-6 hours
60℃ 90 minutes
80℃(just) 60 minutes
PROPERTIES
Volume resistivity 25 ℃ Ohm-cm >1014
Surface resistivity 25 ℃ Ohm >1010
Dielectric strength 25 ℃ Kv/mm 16
Dielectric constant 1KHZ 4.2
Flexural strength kg/mm2 8-10
Impact strength kg/mm2 5-8
Hardness SHORE-D 82
thermal deformation temperature ℃ 80
Water absorption %24h <0.14
Volume shrinkage % 0.26
inflaming retarding UL94 V-0
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE™5404A/B all act 30 kilograms per set. 6 months in an unopened can, kept in cool dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. For accelerating at room temperature, can heating baseboard with electric hot plate. Prevent shake, blow, and ensure surface level up. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE™5404A/B is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be removed by cloth or by using sand to absorb the glue. Once dry the product no longer dissolves in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82377171, Fax: 0086-20-82399962) Yglue™5411A/B-WDESCRIPTION: YGLUE™5411A/B-W is a special liquid resin system, which is used in electronic sealing. It is composed of electric filler, living diluents and super additives. Cured product has excellence gloss surface, similarity agate, its hardness, electric property , inflaming retarding are also very good.
RECOMMEND USAGE: YGLUE™5411A/B-W suit for the all need to sealing, encapsulation, insulating and damp-proof electrons or other kinds of products, especially for the sealing of electromagnetically operated valve.
SURFACE PREPARATION: Ensure the surface preparations, and that the surface is clean and dry, free from dust, perfect degreasing. It is best that first chemical treatment, then coating, so can capture best adhesion.
APPEARANCE & CHARACTER:
YGLUE™5411A-W YGLUE™5411B-W
COLOR white clear
VISCOSITY(25℃, cps) 1700-2000 30-100
SPECIFIC GRAVITY(25℃) 1.5-1.6 1.02
FLASH POINT(℃) 210 >240
MIX RATIO: YGLUE™5411A-W YGLUE™5411B-W
Weight ratio 4 1
POT LIFE: Pot life of mixing YGLUE™5411A-W and YGLUE™5411B-W , depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 50 minutes at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
25℃ 8-10 hours
60℃ 90 minutes
80℃(just) 60 minutes
PROPERTIES
Volume resistivity 25 ℃ Ohm-cm >1014
Surface resistivity 25 ℃ Ohm >1010
Dielectric strength 25 ℃ Kv/mm 16
Dielectric constant 1KHZ 4.2
Flexural strength kg/mm2 8-10
Impact strength kg/mm2 5-8
Hardness SHORE-D 82
thermal deformation temperature ℃ 80
Water absorption %24h <0.14
Volume shrinkage % 0.26
inflaming retarding UL94 V-0
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE™5411A/B-W all act 30 kilograms per set. 6 months in an unopened can, kept in cool dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. For accelerating at room temperature, can heating baseboard with electric hot plate. Prevent shake, blow, and ensure surface level up. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE™5411A/B-W is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be removed by cloth or by using sand to absorb the glue. Once dry the product no longer dissolves in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82377171, Fax: 0086-20-82399962, EMAIL: EPOTEX@21CN.COM).
Updated 2003/8/1 YGLUE™5201A/BDESCRIPTION: YGLUE™5201A/B is a special liquid resin system, which is curing at room temperature. The product after curing has excellent gloss surface, good transparency, high hardness, excellent adhesion and electric property. It can resist water, damp and good chemical resistance. It can also be added color paste to make it colorful.
RECOMMEND USAGE: YGLUE™5201A/B is suitable for the sealing of electronics , especially for LED.
SURFACE PREPARATION: Ensure the surface preparations, and that the surface is clean and dry, free from dust, perfect degreasing. It is best that first chemical treatment, then coating, so can capture best adhesion.
APPEARANCE & CHARACTER:
YGLUE™5201A YGLUE™5201B
COLOR Clear Clear
VISCOSITY(25℃, cps) 700-800 45
FLASH POINT(℃) >140 >140
MIX RATIO: YGLUE™5201A YGLUE™5201B
Weight ratio 2 1
POT LIFE: Pot life of mixing YGLUE™5201A and YGLUE™5201B , depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 35 minutes at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
25℃ 8-10 hours
60℃-80℃ 50-60 minutes
PROPERTIES
Volume resistivity 25 ℃ Ohm-cm 1.6 *10 16
Surface resistivity 25 ℃ Ohm 1.4* 10 15
Dielectric strength 25 ℃ Kv/mm 16~18
Compressive strength kg/mm2 8.4
Tensile strength kg/mm2 5-8
Hardness SHORE-D 78-85
thermal deformation temperature ℃ 100
Water absorption %24h <0.14
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE5201A/B all act 15 kilograms per set. 6 months in an unopened can, kept in cool dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. For accelerating at room temperature, can heating baseboard with electric hot plate. Prevent shake, blow, and ensure surface level up. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE™628A/B is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be removed by cloth or by using sand to absorb the glue. Once dry the product no longer dissolves in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82377171,Fax: 0086-20-82399962, EMAIL: EPOTEX@21CN.COM).
Updated 2003/8/1
Yglue™5116A/BDESCRIPTION: YGLUE 5116A/B is a two-component, room temperature cure, long pot life, fire resistant epoxy encapsulant compound. It is design for potting of capacitors, aquatic animals box device and electrical devices. It has following advantages:
1.Fire resistant, meets UL 94 V-0
2.Good dielectric properties
3.Low shrinkage
4.Low viscosity, fast air release
5.Excellent solvent and water resistance
6.Long pot life
7.Excellent thermal shock and impact resistance
8.Excellent surface appearance
Handling properties:
YGLUE 5116A YGLUE 5116B
COLOR Black brown
VISCOSITY(40℃, cps) 3600 20-100
SPECIFIC GRAVITY(25℃) 1.50 1.02
FLASH POINT(℃) 210 >240
Shelf life (25℃ in sealed container) 12month 12month
MIX RATIO: YGLUE 5116A YGLUE 5116B
Weight ratio 4 1
POT LIFE: Pot life of mixing YGLUE 5116A and YGLUE 5116B, depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 30-40 minutes at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
25℃ 6-8 hours
60℃ 90 minutes
80℃ 60 minutes
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING (as above)
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE 5116A acts 24 kgs per tank and YGLUE 5116B acts 6 kgs per tank. 6 months in an unopened can, kept in cool and dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE 5116A/B is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be remove by cloth or by using sand to absorb the glue. Once dry the product no longer dissolve in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82381150, Fax: 0086-20-82399962, EMAIL: ygplant@21cn.com).
Updated 2003/4/1
YGLUE™5217A/BDESCRIPTION: YGLUE™5217A/B is a double components liquid resin system, which is curing at high temperature used in electronic sealing. It is composed of electric filler, living diluents and super additives. After mixed, it has low viscosity, long service time. Cured product has excellence gloss surface, similarity agate. Its hardness, electric property and inflaming retarding are also very good.
RECOMMEND USAGE: YGLUE™5217A/B suit for the all need to sealing, encapsulation, insulating and damp-proof electrons or other kinds of products, especially for hot protector, filter and the other thermo stable part.
SURFACE PREPARATION: Ensure the surface preparations, and that the surface is clean and dry, free from dust, perfect degreasing. It is best that first chemical treatment, then coating, so can capture best adhesion.
APPEARANCE & CHARACTER:
YGLUE™5217A YGLUE™5217B
COLOR white liquid brings yellow liquid
VISCOSITY(25℃, cps) 1700-2000 10-20
SPECIFIC GRAVITY(25℃) 1.5-1.6 1.02
FLASH POINT(℃) 210 >240
MIX RATIO: YGLUE™5217A YGLUE™5217B
Weight ratio 3 1
POT LIFE: Pot life of mixing YGLUE™5217A and YGLUE™5217B , depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 3.5 hours at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
85℃*2 hours and 100℃ to 110℃*2 hours
if the product has high requests ,it should continue to get older 5 to 6 hours at 90℃
PROPERTIES
Volume resistivity 25 ℃ Ohm-cm >1014
Surface resistivity 25 ℃ Ohm >1010
Dielectric strength 25 ℃ Kv/mm 16
Dielectric constant 1KHZ 3.5-4.2
Flexural strength kg/mm2 11-15
Impact strength kg/mm2 5-8
Hardness SHORE-D 85-90
thermal deformation temperature ℃ >130
Thermal-expansion coefficient cm/cm/ ℃ 45-50*10-6
Water absorption %24h <0.14
Volume shrinkage % 0.26
inflaming retarding &nbs, p; UL94 V-0
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE™5217A/B all act 24 kilograms per set. 6 months in an unopened can, kept in cool dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. For accelerating at room temperature, can heating baseboard with electric hot plate. Prevent shake, blow, and ensure surface level up. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE™5217A/B is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be removed by cloth or by using sand to absorb the glue. Once dry the product no longer dissolves in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82377171, Fax: 0086-20-82399962, EMAIL: EPOTEX@21CN.COM).
Updated 2003/8/1 YGLUE™5317A/BDESCRIPTION: YGLUE™5317A/B is a double components liquid resin system, which is curing at high temperature used in electronic sealing. It is composed of electric filler, living diluents and super additives. After mixed, it has low viscosity, long service time. Cured product has excellence gloss surface, similarity agate. Its hardness, electric property and inflaming retarding are also very good.
RECOMMEND USAGE: YGLUE™5317A/B suit for the all need to sealing, encapsulation, insulating and damp-proof electrons or other kinds of products, especially for hot protector, filter and the other thermo stable part.
SURFACE PREPARATION: Ensure the surface preparations, and that the surface is clean and dry, free from dust, perfect degreasing. It is best that first chemical treatment, then coating, so can capture best adhesion.
APPEARANCE & CHARACTER:
YGLUE™5317A YGLUE™5317B
COLOR black liquid brings yellow liquid
VISCOSITY(25℃, cps) 1700-2000 10-20
SPECIFIC GRAVITY(25℃) 1.5-1.6 1.02
FLASH POINT(℃) 210 >240
MIX RATIO: YGLUE™5402A YGLUE™5402B
Weight ratio 3 1
POT LIFE: Pot life of mixing YGLUE™5317A and YGLUE™5317B , depending upon mixing total weight and operating temperature, generally 100g mixing weight, approximately 3.5 hours at 25℃.
CURING CONDITION: Full curing time, depending upon curing temperature, lowest curing time as follow list:
TEMPERATURE CURING TIME
85℃*2 hours and 100℃ to 110℃*2 hours
if the product has high requests ,it should continue to get older 5 to 6 hours at 90℃
PROPERTIES
Volume resistivity 25 ℃ Ohm-cm >1014
Surface resistivity 25 ℃ Ohm >1010
Dielectric strength 25 ℃ Kv/mm 16
Dielectric constant 1KHZ 3.5-4.2
Flexural strength kg/mm2 11-15
Impact strength kg/mm2 5-8
Hardness &, ;nbs, p; SHORE-D 85-90
thermal deformation temperature ℃ >130
Thermal-expansion coefficient cm/cm/ ℃ 45-50*10-6
Water absorption %24h <0.14
Volume shrinkage % 0.26
inflaming retarding UL94 V-0
RECOMMEND TECHNIC: SURFACE PREPARATION→BASEBOARD PREHEATING (50-60℃) →GLUE MIXING→PROOFING →VACUUM DEFOAMING→CURING
CLEAN UP: Clean all tools and equipment at the end of each days work with organic solvent.
CLEANNESS & MAINTENANCE: Only use commonly cleaning method, e.g. mull dip in clear water, and do not use grinding cleaning tools. Had better not use organic solvent as detergent.
PACKING & STORAGE: YGLUE™5317A/B all act 24 kilograms per set. 6 months in an unopened can, kept in cool dry storage. Seal up for keeping after open the cover as early as possible.
NOTE： Ratio must be just. For accelerating at room temperature, can heating baseboard with electric hot plate. Prevent shake, blow, and ensure surface level up. It is best that be forced after cured 12 hours. Curing at room temperature and dampness, the surface easy display fog, suggest curing at heated.
HEALTH & SAFETY：Avoid swallowing. Wear suitable gloves and eye protection. As the YGLUE™5317A/B is solvent free, it is relatively non-toxic and it is non-flammable. Spills can be removed by cloth or by using sand to absorb the glue. Once dry the product no longer dissolves in organic solvent. Remove from skin before glue dries.
TECHNICAL ADVICE： Please contact KINGYORK (Tel: 0086-20-82377171, Fax: 0086-20-82399962, EMAIL: EPOTEX@21CN.COM).